Product Data Sheet Show all documents

SikaPlast® PH 8394

High range water reducing/ super plasticizing admixture for precast and High-performance concrete

SikaPlast® PH 8394 is an admixture of a new generation based on second-generation polycarboxylate ether polymer with high early strength gains. SikaPlast® PH 8394 is free of chloride & low alkali. It is compatible with all types of cements.

  • Achieve high early strengths
  • Produces Rheo-plastic and Rheo-dynamic concretes having a low water cement ratio
  • Optimize curing cycles by reducing curing time or curing temperatures
  • Eliminate heat curing
  • Eliminate the energy required for placing, compacting & curing (Zero Energy System™)
  • Increase productivity/ reduction in cycle time
  • Improve surface appearance
  • Produce durable precast concrete elements
  • Improved engineering properties, compared to traditional superplasticizer such as early and ultimate compressive and flexural strengths, reduced shrinkage and low permeability.
Product Data Sheet Show all documents

Usage

  • SikaPlast® PH 8394 is suitable for making precast concrete elements at all workability’s including Rheo-plastic or Super workable concrete having fluid consistence, no segregation, a low water binder ratio and, consequently high early and long term strengths
  • Concreting in cold weather
 

Advantages

  • Achieve high early strengths
  • Produces Rheo-plastic and Rheo-dynamic concretes having a low water cement ratio
  • Optimize curing cycles by reducing curing time or curing temperatures
  • Eliminate heat curing
  • Eliminate the energy required for placing, compacting & curing (Zero Energy System™)
  • Increase productivity/ reduction in cycle time
  • Improve surface appearance
  • Produce durable precast concrete elements
  • Improved engineering properties, compared to traditional superplasticizer such as early and ultimate compressive and flexural strengths, reduced shrinkage and low permeability.

Packaging

SikaPlast® PH 8394 is supplied in 225 Kg, 1000 Kg or bulk on request.

Colour

Reddish brown liquid

Product Details

Sustainability / Certifications / Approvals

CERTIFICATES AND TEST REPORTS

ASTM C494 Type B, D & G, EN 934-2 T3.1/3.2, IS 9103: 1999
Product Information

Composition

Modified Poly Carboxylate Ether (PCE)

Shelf life

12 months from date of production if stored properly in undamaged unopened, original sealed packaging.

Storage conditions

Store in dry conditions at temperatures between +10°C and +40°C. Protect from direct sunlight and frost.

Density

~1.09 at 25°C

pH-Value

≥ 6

 

Application

Application Information

Compatibility

SikaPlast® PH 8394 may be combined with many other Sika® products.
Compatible with all types of cements and cementitious materials.
Important: Always conduct trials before combining products in specific mixes and combinations.

Dispensing

SikaPlast® PH 8394 is a ready-to-use liquid which is dispensed into the concrete together with the mixing water. The plasticizing effect and water reduction are higher if the admixture is added to the damp concrete after 70 to 90% of the mixing water has been added. The addition of SikaPlast® PH 8394 to dry aggregate or cement is not recommended.
Thorough mixing is essential and a minimum mixing cycle, after the addition of SikaPlast® PH 8394, of 60 seconds for forced action mixers is recommended.
Consumption

Recommended dosage

Optimum dosage of SikaPlast® PH 8394 should be determined in trial mixes. As a guide, a dosage of 500 gm per 1500kg of cementitious material is normally recommended. Because of variations in concrete materials, job site conditions, and/or applications, dosages outside of the recommended range may be required. In such cases, contact Sika technical service representative.


Effects of over dosage            
A severe over-dosage of SikaPlast® PH 8394 can result in the following:

  • Air entrainment
  • Bleed/segregation of mix, quick loss of workability.
  • Increased plastic shrinkage.

A slight overdosing may not adversely affect the ultimate strength of the concrete and can achieve higher strengths than normal concrete, provided it is properly compacted and cured. Due allowance should be made for the effect of fluid concrete pressure on form work, and stripping times should be monitored.
In the event of over dosage consult with Sika technical service representative immediately.
Application steps

CLEANING

Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be mechanically removed.