Product Data Sheet Show all documents

Sika MonoTop®-122 F

Dual shrinkage compensated, trowelable fibre reinforced thixotropic repair mortar

Sika MonoTop®-122 F  trowelable mortar is a dual shrinkage compensated, thixotropic high strength formulation for structural concrete repairs. Sika MonoTop®-122 F is suitable for placing in thicknesses of 5mm to 50 mm vertically and 5-15mm overhead.

  • Easy to use (only to be mixed with water)
  • Excellent workability
  • Adjustable consistency
  • Structural and Cosmetic repairs
  • Applicable in layers up to 50 mm thickness (vertical surface)
  • Good adhesion strength
  • High abrasion, wear and impact resistance
  • Ideal where the repairs are more than 5 mm
  • Non corrosive, non toxic
  • Increase resistance to salt water, chlorides and carbonation
  • Sprayable - able to repair complex profiles easily with minimal rebound
Product Data Sheet Show all documents

Usage

  • Repair of spalling and damaged concrete in buildings, bridges, infrastructure and super  structure works
  • Use in horizontal, vertical and overhead applications without the need of formworks.
  • Repairing concrete defects like pores, honeycombs and level irregularities.
  • Use as high adhesion render, with high abrasion resistance, waterproof to protect, repair and maintain concrete structures.
 

Advantages

  • Easy to use (only to be mixed with water)
  • Excellent workability
  • Adjustable consistency
  • Structural and Cosmetic repairs
  • Applicable in layers up to 50 mm thickness (vertical surface)
  • Good adhesion strength
  • High abrasion, wear and impact resistance
  • Ideal where the repairs are more than 5 mm
  • Non corrosive, non toxic
  • Increase resistance to salt water, chlorides and carbonation
  • Sprayable - able to repair complex profiles easily with minimal rebound

Packaging

30 kg bag.

Colour

Grey powder.

Product Details

Product Information

Composition

Cement, selected aggregates and additives

Shelf life

6 months from date of production if stored as per recommendation.

Storage conditions

Store properly in undamaged original sealed packaging, in dry conditions at temperatures between +5°C and +40°C.

Bulk Density

~1.3 kg/l  at 27 °C
Technical Information

Compressive Strength

1 day≥ 20 MPa

7 days

≥ 35 MPa

28 days

≥ 50 MPa

* Ambient Temperature : + 30 °C, 70mm Cube

Tensile Strength in Flexure

7 days

≥ 6 MPa

28 days

≥ 9 MPa

* Ambient Temperature : +30 °C

Tensile Adhesion Strength

7 days

≥  8 MPa

28 days

≥ 12 MPa

* Ambient Temperature: +30 °C

Application

Application Information

Mixing Ratio

Water : Powder = 0.15- 0.16 by weight (4.5 – 4.8 ltr of water per bag)

Layer Thickness

Horizontal

Vertical

Overhead

Min.

5 mm

5 mm

5 mm

Max.

50 mm

40-50 mm

15 mm

Ambient Air Temperature

+10°C min. / +40°C max.

Substrate Temperature

+10°C min. / +40°C max.

Pot Life

~ 40 minutes @ +20°C
Consumption

Consumption

~2200 kg/m3

At Water: Powder ratio  0.16

Yield

30 kg of product yields approximately 14 litres of mortar
Application steps

MIXING

Mix powder mechanically in the correct ratio with water with low speed (max. 500 rpm) electric drill to avoid entraining too much air. In case of 2 or more bags at once use forced action mixer.

Put around 80 to 90% of required water in the mixing drum, followed by Sika MonoTop ® 122 F and then add the balance water.

Don’t use concrete tilting mixer.

Do not mix more material which cannot be used within Pot Life. DO NOT ADD EXTRA WATER.

Mix for atleast 3 minutes.

APPLICATION

Apply Sika MonoTop®-122 F manually using traditional techniques

When a bonding primer is used, ensure it is still ‘tacky’ when the repair material is pressed on (‘wet on wet’ technique). When applied manually, press the repair mortar firmly with a trowel, pushing it well on to the substrate.

Smoothening with trowel or finishing by Float or sponge can be done as soon as mortar has started to stiffen.

CURING TREATMENT

Protect the fresh mortar immediately from premature drying using an appropriate curing method e.g. curing compound, moist geotextile membrane, polythene sheet, etc.

CLEANING OF EQUIPMENT

Clean all tools and application equipment with water immediately after use. Hardened material can only be removed mechanically.