Performance Enhancer for Portland Limestone Cement (PLC)

Standards
Mechanical Strength
Strength Enhancer
Workability
Powder Flow Properties
Durability
Approach with SikaGrind LS
Conclusions

Figure 1a: Particle size distribution of 2 PLC with identical limestone content ground in two different types of mill.

In Figure 1a, both PSD graphs show the typical ‘shoulder’ (range 1-10μm) coming from the limestone. The clinker in the ball mill is clearly less ground than in the VRM, which will result in lower mechanical strength. Although the VRM grinds the clinker to a higher degree, the fineness of the limestone is not increased proportionally.

Figure 1b: Fineness parameters of two cements with the same limestone content.

Figure 1b shows fineness parameters of two cements with the same limestone content. The particle size distribution as well as the sieve residue clearly indicates that the high fineness is not only due to limestone but also to well-ground clinker.

Like compressive strength, the workability of concrete (measured as slump or as flow table spread) is positively influenced by finely ground limestone. Bleeding is generally no issue with PLC. The maximum content of limestone which does not negatively influence the workability depends on the quality of the materials and the particle size distribution of clinker and limestone. In general, the use of up to 15% limestone can improve the workability of concrete and mortar (see Figure 3).

Figure 3: Influence of limestone content on workability of mortar (EN 196-1) at constant w/c-ratio and constant compressive strength.

Higher levels of limestone addition require a high specific surface area to compensate the strength loss. Strength enhancers can mitigate the challenge between mechanical strength and workability to a certain extend. Another concept is the use of strength enhancers in combination with a superplasticiser.

The use of superplasticisers which resist the mill ambient conditions and maintain the plasticising effect despite storage in alkaline conditions was pioneered by Sika.⁶ Nowadays this approach is recognised and increasingly applied in practice for the production of portland-limestone cements (see Figure 4).

Figure 4: The workability is essential for the market acceptance of new cements. Low slump can be improved with PCE in the cement additive.

It is well known that portland-limestone cement tends to high cohesive resistance, due to the attraction forces between the fine limestone particles. This can hinder the discharge of trucks or silos because solids can generate stagnant zones.

Many empirical test methods such as the angle of repose, the comparison of bulk density or the packset method7 have been developed to quantify the flow properties of cement. The pack-set index provides a numerical value to control the force required to overcome the vibration-induced consolidation. The test is an aid to routine control during cement production and is not suitable for specification purposes. The higher the pack-set index, the lower the powder flowability.

The awareness of the characteristics of PLC demands a test device which measures clearly defined physical properties. The ring shear tester8 provides defined measurements of the flow properties which are helpful for the development of new cements and the design of silos. In the ring shear tester, the cement sample is contained in an annular shear cell (see Figure 5). A vertical load FN is applied through a thin loading rod on the lid. To shear the sample, the cell rotates relative to the lid (direction ω) and the torque necessary for shearing is determined from the forces F1 and F2 acting in rods fixed to a load beam.

Figure 5: Shear cell of ring shear tester, a Schulze ring shear tester XSMr.

The ratio of consolidation stress to unconfined yield strength is used to characterise the flowability numerically. The larger the flowability number (FFC), the higher the powder flowability.

It is definitely possible to regulate the powder flowability of PLC by cement additives that contain polycarboyxlate ether (PCE) as part of an innovative formulation (Figure 6). Care must be taken to apply the correct dosage. Since the PCEs are very powerful dispersants, the powder flowability can become too high, with negative consequences for instance when cement transport on inclined belts is necessary. The dust load in the grinding station or the capacity of the filter bags can be another limiting factor. The content of PCE in the formulation of SikaGrind can be tailormade to optimise the flow properties.

Figure 6: SikaGrind-870 (PCE-containing strength enhancer) increases the flow properties of cement. The cement samples were prepared in a laboratory mill with constant grinding time, therefore also the fineness increased with the use of SikaGrind.

The cement type can affect the durability of concrete with and without reinforcement. The major topics are environmental actions and the alkali-silica reaction. The environmental actions are classified according to EN 206-1 into the following exposure classes:

XC: Carbonation-induced corrosion;
XS: Chloride-induced corrosion (sea water);
XD: Chloride-induced corrosion (de-icing);
XF: Freeze-thaw attack;
XA: Aggressive chemical environments (e.g. Sulphate).

CEM II/A-LL is used in most European countries for all exposure classes except XA.9 CEM II/B-LL is on the rise and more and more cement producers achieve approvals for this cement class in all exposure classes except XA.

Corresponding to the Standard Specification for Blended Hydraulic Cements ASTM C595/C595M-15, Type IL cement is solely not permitted as a moderate (MS) or high (HS) sulphate resistance cement.

The German association of cement producers initiated a research project with the aim to determine the effects of the particle size distribution on the properties of cements containing limestone and the concretes produced using them^{10, 11}:

A cement plant produced four PLCs with identical constituents in a ball mill by intergrinding. All cements had a content of 30% limestone. The parameters of mill and separator were adjusted to produce different cement surface (Blaine). An identical concrete mix (cement = 300kg/m³, w/c = 0.60) was used to produce cubes which were subjected to the freeze-thaw test according to CEN/TS 12390-9. The concrete must have less than 10% loss of weight after 100 cycles to fulfill the requirement of the standard. Although the cements N°1 and 2 had a significantly higher surface area according to Blaine they did not comply with the requirement whereas cement N°4, with lower Blaine, achieved the target.

Conclusion:

The scaling level does not correspond with Blaine, but the particle size distribution of clinker and limestone is essential.

What is the contribution of SikaGrind to durability?

Tailor-made SikaGrind for PLC are very efficient grinding aids. The tendency of limestone to agglomerate is extremely well reduced by SikaGrind, therefor the share of limestone in the segment of very fine particles is reduced but the fineness of the clinker increased. In this way SikaGrind helps to reduce porosity and chloride diffusion which is an important factor to avoid pitting corrosion. Besides, SikaGrind performance enhancer for PLC improve the workability of concrete – a further positive impact on durability as it avoids the formation of e.g. honeycombs in concrete.

Figure 7: Freezethaw resistance of PLC with different PSD. Blaine is not the decisive factor.

Figure 8: CEM II/A-LL 32.5R. Reduction of 6% clinker content.

Practical experience and results of research are in line with the current trend to portland-limestone cement. Ecological and economical aspects make limestone the most interesting secondary cementitious material. At a certain content of limestone, its positive influence turns and the mechanical strength, the cement powder flowability as well as the durability and the workability of concrete are negatively affected.

Cement additives can be helpful to overcome these issues, but the benefit of strength enhancers is limited. Performance enhancers such as SikaGrind LS can extend the content of limestone in PLC, due to their impact on cement properties and cement production.

1. Locher, F.W.: Zement. Grundlagen der Herstellung und Verwendung, Verlag Bau+Technik, Düsseldorf, 2000, pp. 107.
2. Harrison, A.: Limestone as MAC, International cement review, January 2013, p. 65.
3. Tennis, P.D.; Thomas, M.D.A.; and Weiss, W.J.: State-of-the-art report on use of limestone in cements at levels of up to 15%, SN3148, Portland Cement Association, Skokie, Illinois, 2014, pp. 27-33.
4. De Weerdt, K.: Separate grinding versus intergrinding - State of the art, SINTEF-report SBF BK AO7022, Trondheim, 2007, pp. 12-13.
5. Engelsen, C.J.: Quality improvers in cement making - state of the art, COIN-report 2, SINTEF Building and infrastructure, Oslo, 2008, p. 14.
6. Schrabback, J.M.: Additives for a challenging cement market, World Cement, October 2009, pp 75-78.
7. ASTM C1565, Standard test method for determination of pack-set index of portland cement.
8. Schulze, C.: Flow properties of powders and bulk solids, Wolfenbüttel, 2011, www.dietmar-schulze.de.
9. Swiss society of engineers and architects: Register der frei gegebenen Zemente und Kombination von Zementen und Zusatzstoffen, Zürich, 2015.
10. Verein Deutscher Zementwerke: VDZ-Tätigkeitsbericht 2009-2012, Düsseldorf, 2012, p 89.
11. Verein Deutscher Zementwerke: VDZ-Activity Report 2012-2015, Düsseldorf, 2015, pp 136-139.